TEST |
TEST METHOD |
REQUIREMENTS |
| U.M. |
Value |
|
Thickness |
ASTM D 1813 |
mm |
0.80
- 1.30 |
|
Breaking Strenght |
ASTM D
2208
any direction |
N |
>=
400 |
|
Alongation at 400 N |
ASTM D 2208 |
% |
=< 60 |
| Tear
strength (trapezoid) |
ASTM D
1117
any direction |
N |
>=
44 |
| Seam
fatigue resistance |
FLTM BN
106-02
average of 3 samples
any direction |
mm |
=<
3 |
|
Stiffness in flexing, grain up/down |
(*) IUP 36 |
mm |
>=
4 |
|
Resistance to fade |
SAE J1885, ISO 105-A02AATCC Evaluation Procedure
1
225,6 kJ/m2
488,8 kJ/m2 |
Scale
(1-5) |
>= Rating 4
>= Rating 3 |
|
Resistance to heat aging |
7 days at 100°C +/- 2°
C
ISO 105-A02
AATCC Evaluation Procedure 1 |
Scale
(1-5) |
>=
Rating 4 |
|
Soiling and cleanability |
FLTM BN 112-08, ISO 105-A02AATCC Evaluation Procedure 1 |
Scale
(1-5) |
>=
Rating 3 |
|
Resistance to Cleaning Agents |
FLTM BN 107-01, 10
cycles
- window cleaner with ammonia
- all purpose cleaner
- isopropyl alcohol/water 50% |
Scale
(1-5) |
>=
Rating 4
>= Rating 4
>= Rating 3 |
|
Crocking test |
FLTM BN
107-01
AATCC Evaluation Procedure 3
(Chromatic Transference Scale)
a secco e ad umido (wet ad dry) |
Scale
(1-5) |
>= Rating 4 |
|
Resistance to Migration Staining |
FLTM BN 103-01 |
Scale
(1-5) |
Rating
5 |
| Fogging |
Method A: Photometric
Procedure
SAE J1756
3 h. at 100°C heating,
21°C cooling plate,
post test conditioning 16 h |
% |
>=
60 |
| Fogging |
Method B: Gravimetric
Procedure
SAE J1756
16 h. at 100°C heating
21°C cooling plate,
post test conditioning 4 h |
Weight
of condensate mg |
=<
5 |
|
Resistance to flex at -10°C |
(*) DIN 53351 |
Cycles |
>=
5.000 |
| Satra
vamp flex |
(*) SATRA PM
25
100.000 cycles |
|
No
damage |
| Abrasion
test |
(*) Taber test H18 0,5Kg - ASTM
D3884
- 300 cycles |
|
No
damage |
| Resistance
to pilling wear |
(*) 1 - Taber test cs-10 1 Kg - ASTM D 3884 - 500
cycles
2 - Rubbing Test - DIN 53339
wet = 1.000 cycles |
Grey
scale |
No
damage
>= 4 |
|
Resistance to scuffing |
SAE
J365
Specimen Holder E140-15
200 Cycles (colpi) |
|
No
alteration of color |
| Odor |
FLTM BO 131-01, SAE J369 with 1 liter glass jars |
Scale
(1-5) |
=<
2 |
|
Shrinking |
FLTM BN
105-03
except Heat Cycles 100 +/- 2°C
3 cycles |
% |
=<
5 |
|
Flammability |
ISO 3795, SAE J369
Burn Rate |
mm/minute |
=<
100 |